Atomistic Indicators of the Ductile-to-Brittle Transition in Polycrystalline Tungsten: Temperature and Rhenium Effects on Crack-Tip Plasticity

Abstract

The fracture response of body-centered-cubic tungsten is governed by competition between crack-tip instability and dislocation-mediated plastic accommodation. Molecular dynamics (MD) simulations are used to examine edge-cracked polycrystalline W and W-Re under displacement-controlled Mode-I tension from 300-1800 K at a strain rate of 5 x 10^8 s^-1. Heating pure W reduces the instability stress, effective specimen stiffness, and pre-instability volumetric work density, while the instability strain remains comparatively scattered. A normalized work-loss metric derived from the pre-instability work gives a broad sigmoid crossover marker, T*_MD ~ 870 K, characteristic of the simulated geometry and high-rate loading conditions. Among the available W-Re compositions, W-10Re shows greater pre-instability deformation and work accumulation than pure W across most temperatures, while the maximum-stress response remains strongly temperature- and composition-dependent. Changes in retained dislocation character and near-tip activity indicate that Re modifies the crack-tip plastic-accommodation pathway rather than producing a simple strength increase. Common-state analysis further shows that Re alters the retained 1/2<111>line character and the temporal distribution of near-tip dislocation activity without uniformly increasing the local dislocation population. These coupled mechanical and defect-structure changes provide atomistic indicators of a high-rate ductile-to-brittle transition (DBT), but not a direct prediction of experimental DBTT. A separate OpenDiS/pydis calculation demonstrates source-like bow-out and heterogeneous dislocation-network development in crack-free polycrystalline W, providing mesoscale context without implying direct quantitative MD-DDD coupling.